| Customization: | Available |
|---|---|
| Feature: | Oxidative Degradable |
| CAS No.: | 9003-07-0 |
|
Still deciding? Get samples of US$ 1/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
|
Physical properties of
|
The test conditions
|
The test method
|
The test results
|
unit
|
|
Density/specific gravity
|
|
ASTM D792
|
0.898
|
G /cm sharp
|
|
Melt flow rate (melt flow rate)
|
230°C/2.16 kg
|
ASTM D1238
|
3
|
g/10 min
|
|
Shrinkage rate - flow
|
23°C
|
Internal methods
|
1.4 to 1.8
|
%
|
|
Mechanical properties of
|
The test conditions
|
The test method
|
The test results
|
unit
|
|
Tensile strength
|
The yield, 23 ° C
|
ASTM D638
|
25
|
Mpa
|
|
elongation
|
Fracture, 23 ° C
|
ASTM D638
|
> 200
|
%
|
|
Bending modulus
|
23°C
|
ASTM D790A
|
1080
|
Mpa
|
|
Thermal performance
|
The test conditions
|
The test method
|
The test results
|
unit
|
|
Thermal deformation temperature under load
|
1.8mpa, unannealed, 6.35mm
|
ASTM D648
|
110
|
°C
|
|
Impact properties
|
The test conditions
|
The test method
|
The test results
|
unit
|
|
Notched impact strength of cantilevered beam
|
-20°C, 3.18 mm
|
ASTM D256
|
93
|
J/m
|
|
|
23°C, 3.18 mm
|
ASTM D256
|
590
|
J/m
|
|
The injection
|
The test conditions
|
The test method
|
The test results
|
unit
|
|
Processing (melt) temperature
|
|
|
From 180 to 230
|
°C
|
|
Mold temperature
|
|
|
30 to 50
|
°C
|
|
Injection pressure
|
|
|
2.94 - 5.88
|
Mpa
|
|
hardness
|
The test conditions
|
The test method
|
The test results
|
unit
|
|
Rockwell hardness
|
R , 23°C
|
ASTM D785
|
80
|
|
|
flammability
|
The test conditions
|
The test method
|
The test results
|
unit
|
|
UL flame retardant rating
|
|
UL 94
|
HB
|