| Material: | Laminated Material |
|---|---|
| Usage: | Packaging Film, Food Cling Film |
| Processing Type: | Multiple Extrusion |
| Transparency: | Transparent |
| Feature: | Moisture Proof |
| Hardness: | Soft |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Combining the processability of vinyl polymer with the blocking effect of vinyl alcohol polymer, our Ethylene Vinyl Alcohol Copolymer (EVOH) offers excellent gas, odor, fragrance, and solvent blocking capabilities. Its thermal stability makes it ideal for reusable multilayer containers.
EVOH is the most widely used high barrier material, available in various film types including biaxial tensile, aluminum evaporation, and adhesive coating. Its excellent gas barrier, transparency, gloss, and mechanical strength make it perfect for aseptic packaging and other applications.
In the field of packaging, EVOH is used in hard and flexible packaging, aseptic packaging for food products, and packaging for solvents, chemicals, and electronic components. It can replace glass and metal containers in food packaging, offering superior barrier performance.
Our EVOH products are versatile, suitable for film production, cosmetic packaging, floor heating pipes, jelly cups, and pesticide bottles. As a non-toxic environmental protection material, EVOH enhances quality of life while contributing to environmental protection.
Experience the benefits of EVOH Barrier Material from GYF BIOTECH LTD. today!
| EVASIN EV2951F DATA SHEET | ||||
| 29 mole%Ethylene Vinyl Alcohol Copolymer | ||||
| Application | ||||
| EV2951F with lower melt flow index is specially designed for co-extrusion cast or blown application.This resin can also be used in bottle and pipe application. |
||||
| General Property | ||||
| Item | unit | Test Method | Value | |
| Mechanical Properties | ||||
| Tensile strength at yield | MPa | ISO 527 | 85.8 | |
| Tensile strength at break | MPa | ISO 527 | 35.7 | |
| Elongation at break | % | ISO 527 | 19.6 | |
| Young's modulus | MPa | ISO 527 | 4,580 | |
| Flexural modulus | MPa | ISO 178 | 4,300 | |
| Flexural strength | MPa | ISO 178 | 130 | |
| Charpy impact strength | KJ/m² | ISO 179-1 | 2.27 | |
| Rockwell hardness | M | ISO 2039-2 | ||
| Density | g/cm² | ISO 1183 | 1.19 | |
| Thermal Properties and Melt Characteristics | ||||
| Melting point | ºC | ISO 11357 | 188 | |
| Crystalization point | ºC | ISO 11357 | 163 | |
| Glass transition point | ºC | ISO 11357 | 62 | |
| icat Softening Poin | ºC | ISO 306 | 175.3 | |
| Melt flow index | g/10min(2160g,190ºC) | ISO 1133 | ||
| g/10min(2160g,210ºC) | ISO1133 | 2.5 | ||
| Gas Barrier Properties | ||||
| O2Transmission Rate at 20ºC 0%RH at 20ºC 65%RH at 20ºC 85%RH |
cm³.20μm/m².24Hrs.atm | ISO 14663-2 | 0.1 0.2 1.3 |
|
| Water Vapor Transmission Rate | cm³.30μm/m².24Hrs.atm at 40ºC90%RH |
ASTME96-E | 55 | |
Combining the processability of ethylene polymer with the barrier effect of ethylene alcohol polymer, ethylene-vinyl alcohol copolymer offers excellent processing performance and exceptional blocking effect on gas, odor, fragrance, solvent, and more. Its thermal stability when combined with ethylene makes multilayer containers with EVOH barrier layers fully reusable. These features make plastic containers with EVOH barrier layers a superior choice, replacing traditional glass and metal containers in food packaging.